graphite fiber packing

Temperature -100-+300
Pressure 35MPa
linear velocity 15m/s
PH Value 2-12

Carbon Fiber Packing
The packing is woven of strong carbon fiber after softening treatment and impregnated with the mixture of fine graphite po

1.Max. working temperature: -75 ~ 260oC
2.Max. working pressure:1.5 Mpa(rotary pump)
3.Cross Section: 1/8" ~ 2"
4.Density: 1.45 ~ 1.55g/cc

1. Packing made of synthetic fiber yarns
2. Packing needs impregnating with block agents, lubricants
3. Economic seal packing choice

Texturized fiberglass braided round packing, diameter: 3mm-50mm, roll length:10m-200m, weight: 25g/m-1950g/m, continuous temperature resistance:550℃

Carbon Packing is made from carbonized fiber yarn treated with graphite particles, and then is braided to form packing.

silica gel packing is made of silica core + glass fiber casing+ silicone coating,

Aramid fiber packing kevlar fiber packing nomex fiber packing are available from China FEITE Sealing Material Co Ltd

JX305 CARBON FIBER PACKING
The packing is woven of strong carbon fiber after softening treatment impregnation with the mixture of fine graphite

info(at)acsealing com Pure carbon fiber packing is Braided of caebon fiber? impregnated with proprietary lubricants and PTFE,? it has High pressure an

AT511L1 Comparing with the yellow aramid fiber packing, the Nomex Fiber Packing does not require high rigidity of the shafts.

High strength carbonized fiber packing is mede from imported carbonized fiber. And it is impregnated with PTFE latex, nami level graphite powder or ot

Carbonized Fiber Packing & Ring,Gland Packing & Ring

Braided from high-performance KynolTM ( NovilidTM or PhenolicTM) fiber impregnated with PTFE lubricant, good mechanical properties combining softness

Braided from strong carbon continuous yarns after softening, impregnated with proprietary lubricants and graphite particles, which fill voids

PTFE fiber packing is a pure yarn packing braided into square cross section and impregnated with PTFE dispersion.
High cross-sectional density an

Made of polyacrylonitrile filament through reinforcing, braiding and impregnated with PTFE.
Size: 3mm--50mm

Price:US$0.3;Productivity:6000KGS PER DAY;Min. Order:1 KG;Packing:WOODEN CASE;Transportation:TIANJIN;DeliveryDate:ONE WEEK;PaymentType:T/T;Trademark:

Carbon fiber packing is weaved by carbon fiber,then soak it in PTFE emulsion with graphite powder and thermostable lubrication.

This packing is a multi-yarns packing. The corners of packing are made of aramid fiber yarns impregnated with graphite PTFE.

Kevlar fiber packing is made of Du Pont's Kevlar yarn impregnated with PTFE dispersion and processed with lubricant.braided into square cross section

Ramie Fiber Packing With Grease Impregnation is applicable to the media such as water, oil, weak acid, alkali, mortar, pulp, etc. and feed pump, centr

Temperature -100-+280
Pressure 35 MPa
linear velocity 12m/s
Chemical Resistance PH value 2-12

Texturized fiberglass braided 701920102 dimention: 5x5mm-50x50mm, roll length: 10m-200m, weight: 25g/m-2250g/m, Continuous temperature Resistance 550C

An economical universal packing, suitable for rotating and reciprocating pumps, valves, agitators etc with water, sea-water, alcohol, etc.

1) pH value: 0 - 14
2) Linear speed: 0 -2m/s
3) Cross Section: 1/8" ~ 2"
4) Density: 1.10 ~ 1.30g/cc
5)Density :1.50 ~ 1.60g/cc(with inconel

info(at)acsealing com High carbon fiber packing is made ofimported high-modulus carbon fiber, immerses quasinmlevel graphite, can prevent the lea

WEALSON Pure Ptfe Fiber Packing is made of pure PTFE yarn, there are no PTFE latex and lubricant.

WEALSON Pure Ptfe Fiber Packing is made of pure PTFE yarn, there are no PTFE latex and lubricant.

High quality fiber pulp Mushroom packing design
KINYI-A Professional Manufacturer of Molded Pulp Products