carbon graphite packing

Special graphite filled P.T.F.E. fiber is braided with P.T.F.E. Fiber. It is suitable for various revolving and reciprocating machineries.

carbon fiber packing
carbonized fiber packing
carbon fiber with ptfe
carbon fiber with graphite

It is a high-quality baided packing made of PTFE yarns fiberwith incorporated graphite and the reinforced reinforced corner yarns of Aranmid fiber

1. Packing made of Graphite yarns or Carbon fibres
2. Graphite yarns are reinforced with fibres
3. Carbon fibre packings require impregnation

Graphite packing with carbon fiber corners
1. More resistant to extrusion
2. Increase the pressure handing capabilities.

Price:US$3.0;Productivity:8000KGS PER DAY;Min. Order:5 KGS;Packing:WOODEN;Transportation:SEA;DeliveryDate:5DAYS;PaymentType:T/T;Trademark:QS;Specific

Density from 1.10 to 1.60g/cm3. temperature: 650℃. pressure: 25Mpa. with carbon fiber, glass fiber, SS304 wire, inconel wire reinforcement.

Graphite packing with carbon fiber corners is a multi-fiber packing, braided from expanded graphite yarns and carbon fibers.

Reinforced with Carbon Graphite is pure flexible graphite packing reinforced in all four corners with high strength Carbon fiber and impregnate PTFE

braided from unique low friction carbon fibre yarn, it is impregnated with PTFE and graphite as additional lubricant

Graphite Packing With Carbon Fiber Corner Packing
Density (g/cm3):1.1

AT305L1 Graphite packing with carbon fiber corners.
Diagonally braided from flexible graphite, reinforced at the corners with high quality

Flexible graphite carbon fibre packing

Diagonally braided from expanded flexible graphite, reinforced at the corners throughout with high quality carbon fiber. This corners and body make it

Expanded Graphite Packings
76-022 Expanded Graphite Packing | 76-022A Expanded Graphite Packing | 76-022B Carbon and Graphite Packing | 76-022C Car

Graphite packing with carbon fiber corners

Temperature -100-+600
Pressure 35MPa
Chemical resistance PH valve 0-14

1) Operational temperature: -200 - 850oC
2) Operational pressure: 6 - 30Mpa
3) pH value: 0 - 14

1--composed of PTFE yarn
2--great tear strength & high thermal conductivity
3--low coeffecient and friction

The pastins braided by technology of braiding around a core (or cores) or mutipie sieve braid etc.have there perfect safe properties on sealing. They

Graphite packing is woven of cotton fiber reinforced graphite formed.It is flexibility, compressibility and corrosion-resistant.

Productivity:30000METERS;Min. Order:100 METER;Packing:CARTON ;Transportation:Sea shipment ;DeliveryDate:IN 20 DAYS ;PaymentType:T/T,D/P,L/C ;Tradema

auto carbon fiber soaked graphite packing

High Carbon Packing Withe PTFE Impregnated & Coated Graphite
Density (g/cm3):1.4

Flexible graphite carbon fibre packing

Aramid Fiber Packing with An Inert Lubricant
White PTFE Packing with Aramid Fiber Corners
Black PTFE Packing with Aramid Fiber Corners

Variety: all kinds of graphite packing, graphite packing ring, spiral wound gasket, graphite thread

graphite ring:
1. bore size:3-200mm
2.outside Dia:5-240mm
3.Density:1.5g/cm3
4. compressive strength:40Mpa

 
Chemical stability and self-lub

DESCRIPTION:
RS-5013 Expanded graphite braided packing is made from expanded pure graphite yarn, braided into packing through all kinds of ...