Graphite Electrode is made of high-quality low ash materials, such as CPC, NC and coal pitch.after calcining,burdening,kneading,forming,baking and pressure impregnation, graphitization and then precision machined with professional CNC machining.such of the products own characteristics with low resistivity, good electrical conductivity ,low ash, compact structure,good anti oxidation and high mechanical strength, Widely used in LF, EAF for steel making industry, Non-ferrous industry, silicon and phosphorus industry.so it is the best conductive material for electric arc furnace and smelting furnace. Application Of Graphite electrodes: Graphite electrodes are used mainly in ladle furnaces,electric-arc furnace steelmaking,Yellow phosphorus furnace , Industrial silicon furnace or melting copper. They are presently the only products available that have the high levels of electrical conductivity and the capability of sustaining the extremely high levels of heat generated in this demanding environment.High Quality NC in HP&UHP graphite electrode,ensure the electrode application is perfect. Graphite electrodes are also used to refine steel in ladle furnaces and in other smelting processes. Characteristics Of Graphite electrodes: Our graphite electrodes are with low electric resistance, high density, high anti-oxidation capability, precise machining accuracy, especially with low sulphur and low ash will not give steel second time
Specification of High Quality UHP Graphite Electrode Sales From China
The Length & Diameter & Permissible Deviation of Graphite Electrode
| Nominal Diameter | Actual Diameter | Length (mm) | Tolerance | ||||
| MM | Inch | Poppy | Mines | The Minimum Size Of The Black Part | Length | Short Length | |
| 75 | 3 | 78 | 73 | 72 | 1400/1600 | ± 100 | -275 |
| 100 | 4 | 103 | 98 | 97 | 1400/1600 | ||
| 130 | 5 | 132 | 127 | 126 | 1400 | ||
| 150 | 6 | 154 | 149 | 146 | 1400/1600/1800 | ||
| 175 | 7 | 180 | 174 | 172 | 1400/1600 | ||
| 200 | 8 | 205 | 200 | 197 | 1600/1800 | ||
| 225 | 9 | 230 | 225 | 222 | 1600/1800 | ||
| 250 | 10 | 255 | 251 | 248 | 1600/1800 | ||
| 300 | 12 | 307 | 302 | 299 | 1600/1800/2000 | ||
| 350 | 14 | 357 | 352 | 349 | 1600/1800/2000 | ||
| 400 | 16 | 409 | 403 | 400 | 1600/1800/2000/22000 | ||
| 450 | 18 | 460 | 454 | 451 | 1600/1800/2000/22000 | ||
| 500 | 20 | 511 | 505 | 502 | 1600/1800/2000/22000 | ||
| 550 | 22 | 562 | 556 | 553 | 1800/2000/2200/2400 | ||
| 600 | 24 | 613 | 607 | 604 | 2000/2200/2400/2700 | ||
| 650 | 26 | 663 | 659 | 656 | 2000/2200/2400/2700 | ||
| 700 | 28 | 714 | 710 | 707 | 2000/2200/2400/2700 | ||
★ Technical Characteristics of Graphite Electrode RP, HP, UHP
| Name | Unit | Nominal Diameter | ||||||
| UHP Ultra-High-Power | HP Superstrong | RP Conventional Power | ||||||
| ≤Φ400 | ≥Φ450 | ≤Φ400 | ≥Φ450 | ≤Φ300 | ≥Φ350 | |||
| Resistivity | Electrode | ΜΩ · m | ≤5.5 | ≤6.5 | ≤8.5 | |||
| Nipple | ≤4.5 | ≤5.5 | ≤6.5 | |||||
| Flexural Strength | Electrode | MPa | ≥11.0 | ≥10.5 | ≥9.8 | ≥8.5 | ≥7.0 | |
| Nipple | ≥20.0 | ≥16.0 | ≥15.0 | |||||
| Elastic Modulus | Electrode | GPa | ≤14.0 | ≤12.0 | ≤9.3 | |||
| Nipple | ≤18.0 | ≤16.0 | ≤14.0 | |||||
| Density | Electrode | g / cm3 | ≥1.66 | ≥1.67 | ≥1.62 | 1.6 | ≥1.53 | ≥1.52 |
| Nipple | ≥1.75 | ≥1.73 | ≥1.69 | |||||
| Coefficient Of Thermal Expansion | Electrode | 10-6 / ºC | ≤1.5 | ≤2.4 | ≤2.9 | |||
| Nipple | ≤1.4 | ≤2.2 | ≤2.8 | |||||
| ASH | % | ≤0.3 | ≤0.3 | ≤0.5 | ||||
| Note: 1.Koeffitsient ash content and thermal expansion as the reference index, the coefficient of thermal expansion (100 ºC ~ 600 ºC), Custom manufacturing. | ||||||||
★ Technical Characteristics of High Density Graphite Electrode (HD)
| Name | Unit | Nominal Diameter | ||||||
| 75-200 mm | 250-300mm | 400-500mm | ||||||
| top grade | first grade | top grade | first grade | top grade | first grade | |||
| Resistivity (Not More Than) | Electrode | ΜΩ · m | 8.0 | 9.0 | 8.0 | 9.0 | 8.0 | 9.0 |
| Nipple | 7.5 | 7.5 | 7.5 | |||||
| Flexural Strength(not less than) | Electrode | MPa | 10 | 9 | 8 | |||
| Nipple | 13 | 13 | 13 | |||||
| Elastic Modulus(no more) | Electrode | GPa | 12 | 12 | 12 | |||
| Nipple | 14 | 14 | 14 | |||||
| Density(not less than) | Electrode | g / cm3 | 1.58 | 1.58 | 1.58 | |||
| Nipple | 1.68 | 1.68 | 1.68 | |||||
| Coefficient Of Thermal Expansion (No More) | Electrode | 10-6 / ºC | 2.7. | 2.7. | 2.7. | |||
| Nipple | 2.5 | 2.5 | 2.5 | |||||
| Ash Content (not more than) | % | 0.3 | 0.3 | 0.5 | ||||
| Note: 1. The coefficient of ash content and thermal expansion as a reference index. | ||||||||
★ Technical Characteristics of a Quasi-Superhigh-Gauge Graphite Electrode (EGPK-SHP)
| Name | Unit | Nominal Diameter (mm) | ||
| 300, 350, 400 | 450, 500 | |||
| Resistivity (not more than) | Electrode | ΜΩ · m | 6.2 | 6.5 |
| Nipple | 5.5 | 5.5 | ||
| Flexural Strength(not less than) | Electrode | MPa | 10.5 | 10 |
| Nipple | 16 | 16 | ||
| Elastic Modulus(no more) | Electrode | GPa | 14 | 14 |
| Nipple | 18 | 18 | ||
| Density(not less than) | Electrode | g / cm3 | 1.65 | 1.64 |
| Nipple | 1.72 | 1.7 | ||
| Coefficient Of Thermal Expansion (no more) | Electrode | 10-6 / ºC | 1.5 | 1.5 |
| Nipple | 1.4 | 1.4 | ||
| Ash Content (not more than) | % | 0.3 | 0.3 | |
| Note: 1. Zonality as a reference index. | ||||
Applications
1. Low electric resistance
2. High density
3. Good electrical conductivity
4. High anti-oxidation capability
5. Precise machining accuracy
6. Low sulphur and low ash, not give steel second time impurity