kevlar ptfe graphite packing

1. Max. working temperature: -75 ~ 280oC
2.Max. working pressure: 35Mpa (valve)
3. Cross Section: 1/8" ~ 2"
4. Density: 1.65 ~ 1.75g/cc

graphite ptfe packing with aramid is combined with graphite PTFE and aramid,it have more lubricating performance and thermal conductivity

Graphited PTFE AIFLON 2320A or B Graphifed PTFE (GPTFE)yarn.The packing is soft.There are no free particles of graphite on surface and therefore no co

1- perfect corrosion resistance
2-can be used at dynamic sealing location

Braided from pure Graphite PTFE yarn without any lubrication. It is non-contaminating packing.

Braided from graphited PTFE (gPTFE) plain yarn. The packing is soft, with low density There are no free particles of graphite on surface.

Graphite PTFE Packing is abraided packing made of PTFE yarn containing graphite.It is recommended for shafts for almost all chemicals.

graphite PTFE packing (also known as Black PTFE packing) is a resin with PTFE seal made of graphite composite packing, graphite and PTFE as a result

Reinforced PTFE/graphite braided packing with heat-resistant lubricant impregnated is to used more efficiently with revolving pump in water plants

Graphite PTFE yarn is developed from high quality PTFE resin ,graphite powder and thermostable lubricant by special processing.

Price:US$5.0;Min. Order:1 kg;DeliveryDate:10days;Trademark:HuaKai;

1- perfect corrosion resistance
2-can be used at dynamic sealing location

Graphite packing impregnated PTFE

Graphite PTFE packing with aramid corner is braided by kevlar and the fiber which composite with graphite and PTFE, Aramid strengthen in the corners

Special graphite filled P.T.F.E. fiber is braided with P.T.F.E. Fiber. It is suitable for various revolving and reciprocating machineries.

1. Working temperature: -200 ~ +260 centigrade
2.Linear speed: 1.5M/S(reciprocating pump)
3.PH value: 0-12
4.Cross Section: 1/8" ~ 2"

PTFE graphite fiber braided packing (Balck PTFE packing )consists of PTFE yarn containing graphite panicles.

Flexible Graphite Packing with PTFE Corner

Braided with PTFE graphite yarn and blended with silicone rubber core atcentral positins,having excellent compression-compensating power.

It is a high-quality baided packing made of PTFE yarns fiberwith incorporated graphite and the reinforced reinforced corner yarns of Aranmid fiber

High-quality combination of PTFE with incorporated graphite and additional reinforcement of sliding surface of aramid yarn. Good sliding velocity and

Productivity:negotation;Packing:wood case;DeliveryDate:20 days;PaymentType:T/T;Trademark:Rilson;CoopCompany:Rilson;

AT513 It is an excellent packing interwoven from PTFE yarns infiltrated with graphite, and Kevlar filaments. Specially designed for rotating pumps

1--Reinforced with aramid yarn
2--Stand high temp,& pressure
3--Good velocity and theral conductivity

PTFE-graphite with kevlar fiber corner braided packing
Density (g/cm3):1.40-1.45

, , cotton packing, Packing series: expanded graphite packing,reinforced graphite packing , Die-formed graphite ring packing(expanded graphite molded

Asbestos packing, PTFE Packing, Graphite Packing, Asbestos Rubber or Oil Packing, Kevlar Fiber Packing, Carbon Fibre Packing

Aramid Fiber Packing with An Inert Lubricant
White PTFE Packing with Aramid Fiber Corners
Black PTFE Packing with Aramid Fiber Corners

> Tough and durable
> heat and chemical resistant.

1. Made from graphite-PTFE compound with lubricant very good operating efficiency.
2. Gentle treatment of shafts.